Identification of Fibreglasses Fire Danger Indicators and Strength Characteristics Dependences from Formation Conditions

Konstantin A. Afanasenko, Aleksandra P. Mihaylyuk, Yuriy P. Klyuchka

Abstract


Key words:C/H ratio, the coke rest, oxygen index, ignition temperature, bending strength, molding parameters

 

Annotation:It is investigated fiberglass molding on an example the epoxyphenol binder. It is established that fiberglass oxygen index, ignition temperature and bending strength based on the examined binders depends on the molding parameters. The dependences regression models are developed. It is performed formation parameters optimization.


Volltext:

PDF (Russian)

Literaturhinweise


Composite polymeric materials creation principles: AA. Berlin, AA. Volfson, VG. Oshmyan, NS. Enikolopov. Moscow, Chemistry, 1990; 240.

Mihaylin YuA. Constructional polymeric composite materials. Moscow, Scientific bases and technologies, 2008; 822.

Afanasenko KA. Decrease in indicators of fire danger of polymeric composite materials by application binding, inclined to carbonization: KA. Afanasenko, PA. Bilyim, AP. Mihaylyuk: Fire safety problems, 2013, № 34; 12-17.

Afanasenko KA. Binding for fibreglasses with the lowered fire danger indexes: KA. Afanasenko, PA. Bilyim: “Technologies of a Technosphere” Safety Internet magazine (http://ipb.mos.ru/ttb), 2014, № 6 (58).

Lapitskiy VA. Physicomechanical properties of epoxy polymers and fibreglasses: VA. Lapitskiy, AA. Kritsuk. Kiev, Scientific thought, 1986; 96.


Refbacks

  • Im Moment gibt es keine Refbacks